VYPET VNT 635A
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cWTwQG_VYPET-VNT-635A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet 635A is a 35 % glass reinforced PET injection molding compound designed for electrical and structural applications with a very glossy surface Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 0.40 | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.80 | % | ASTM D955 |
| Ash Content | 35 | % | ASTM D2854 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 140 | MPa | ASTM D638 |
| Flexural Modulus 2 | 10000 | MPa | ASTM D790 |
| Flexural Strength 3 | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 225 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Pressure | 55.0 - 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 75 | rpm |
| Injection instructions |
|---|
| Back Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HG3201SK2 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| UBE Nylon 5034 MTX1 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Formolon® 685 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| Hifax CA 1110 G4 LS/4 | LyondellBasell Industries | PP Copolymer | Hifax |
| Hanwha Total PP BI451 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |