CYCOLOY™ EX58 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cW3Q3K_CYCOLOY-EX58-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High impact ABS for sheet extrusion and blow molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2080 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 40.0 | MPa | ASTM D638 |
| Fracture | 30.3 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.1 | % | ASTM D638 |
| Fracture | 32 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2160 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 300 | J/m | ASTM D256 |
| 23°C | 430 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 37.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 93.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 7 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1400 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 171 - 199 | °C | |
| Cylinder Zone 2 Temp. | 182 - 221 | °C | |
| Cylinder Zone 3 Temp. | 188 - 227 | °C | |
| Cylinder Zone 4 Temp. | 199 - 238 | °C | |
| Adapter Temperature | 204 - 249 | °C | |
| Melt Temperature | 216 - 260 | °C | |
| Die Temperature | 204 - 249 | °C |
| Extrusion instructions |
|---|
| Roll Stack Temp - Bottom: 99 - 104 °CRoll Stack Temp - Middle: 93 - 104 °CRoll Stack Temp - Top: 88 - 93 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1281-60D | RTP Company | TPU-Polyester | RTP |
| RheTech Polypropylene HP800-706UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Tenac™ MG210 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Mytex® AX1162 | Mytex Polymers | PP, Unspecified | Mytex® |
| DAI-EL™ G-101 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |