Kingfa MAC-451 UV
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cVxyMD_Kingfa-MAC-451-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa MAC-451 UV is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main characteristics of Kingfa MAC-451 UV are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -25°C, 3.20 mm | 260 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 125 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 115 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Weather Resistance, ASTM D4459, 200hr xenon lamp: 2 delta E |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 105 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure | 0.00 - 10.0 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® M690 | Lubrizol Advanced Materials, Inc. | PETG | Stat-Rite® |
| NYCOA Polyamide 1838 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| FHR EPS 40-3640 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Petrothene® LR763011X01 | LyondellBasell Industries | HDPE | Petrothene® |
| Sylvin 8490-70UV Natural | Sylvin Technologies Incorporated | CPE | Sylvin |