LUBEMID B27 GF50 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cV8RmD_LUBEMID-B27-GF50-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6 natural first choice. With glass fibres 50% |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 to 1.57 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 to 12500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 160 to 170 | MPa | |
| Break | 160 to 170 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 1.5 to 2.0 | % | |
| Break | 1.5 to 2.0 | % | |
| Flexural Modulus 1 | 10500 to 11500 | MPa | ISO 178 |
| Flexural Stress 2 | 240 to 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 to 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 to 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 140 to 150 | J/m | ASTM D256A |
| 23°C 3 | 130 to 140 | kJ/m² | ASTM D256 |
| 23°C | 12 to 18 | kJ/m² | ISO 180/A |
| 23°C 4 | 14 to 15 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 100 to 110 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 210 to 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 215 to 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 200 to 210 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 210 to 220 | °C | ISO 306/A120 |
| -- | 205 to 215 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT079 | Sasol Polymers | LDPE | Sasol Polymers PE |
| Sumiflex® QE QE518AEA | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| NYLOY® UB-0010N-V G55N2N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Sylvin 8376-92UV Yellow 4209 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX987 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |