Moplen HP544T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cUqMkw_Moplen-HP544T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen HP544T is a polypropylene homopolymer. With its high flow, excellent dimensional stability, and good surface finish, this grade is especially suitable for thin wall injection molding. Its ease of processing creates parts with lower built-in stress, thereby allowing greater flexibility in part design. Potential end use applications include fast cycle injection moulding of food containers, drinking cups, thin wall cylinders, and complex items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 60 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 37.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 1700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 26 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 119 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ300G6 | Polyram Ram-On Industries | PC | RAMTOUGH |
| NuSil MED-360 | NuSil Technology | Silicone | NuSil |
| ELASTOSIL® N 9111 WHITE | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| Geon™ Vinyl Rigid Extrusion L6701 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Lupox® LW5402A | LG Chem Ltd. | PC+PBT | Lupox® |