LNP™ THERMOCOMP™ LF006 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cTSV0g_LNPTHERMOCOMPLF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF006 is a compound based on Polyetheretherketone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound LF-1006 BK905 Product reorder name: LF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.54 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13200 | MPa | ASTM D638 |
| -- | 13100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 176 | MPa | ASTM D638 |
| Fracture | 175 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.0 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| -- | 12700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 241 | MPa | ASTM D790 |
| -- | 264 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 3 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 14.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | > 299 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | > 240 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | > 299 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | > 240 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.780 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® 641 IBS (20 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Bergamid™ A70 G35 UF SO | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Epoxies, Ect. 50-3170 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Hanwha Total PP FB33 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Tunhe PET TH103 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |