LNP™ THERMOCOMP™ DF0029ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cSzGXF_LNPTHERMOCOMPDF0029ERcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1002 EM FR MR Product reorder name: DF0029ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.68 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.67 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 83.4 | MPa | ASTM D638 |
| Yield | 84.0 | MPa | ISO 527-2 |
| Fracture | 79.3 | MPa | ASTM D638 |
| Fracture | 81.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.9 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2 |
| Fracture | 5.5 | % | ASTM D638 |
| Fracture | 4.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4140 | MPa | ASTM D790 |
| -- | 4100 | MPa | ISO 178 |
| Flexural Stress | 129 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 870 | J/m | ASTM D4812 |
| 23°C 3 | 59 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.3 | J | ASTM D3763 |
| -- | 7.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 142 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 2.78 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 136 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP515M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Moplen EPQ30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| LubriOne™ SF-20AF/10T BLACK | PolyOne Corporation | PPS | LubriOne™ |
| Petrothene® GA601032 | LyondellBasell Industries | LLDPE | Petrothene® |
| Edistir® N 3782 | Versalis S.p.A. | PS (GPPS) | Edistir® |