Elastofoam® 38100R / 3120T Datasheet,PUR, Unspecified,BASF Corporation-SHANGHAI SUSHENG

Message
Low density I-skin foam system (natural color) HFC 245fa-blown, two-component microcellular polyurethane foam system designed for molding of miscellaneous Integral Skin articles that require good skin at relatively low molded densities. Depending on the application requirements and the processing conditions this system can provide Exceptional skin formation when casted in metal tools at low mold temperatures Wide range of molded densities from 10 to 25 pcf Hardness range from 10 to 70 Shore A Wide processing window on both low-pressure and high-pressure equipment

General Information
Features	Low density Workability, good
Uses	Foam Application in Automobile Field Car interior parts

Physical	Nominal Value	Unit	Test Method
Density			ASTM D1622
-- ¹	0.256	g/cm³	ASTM D1622
-- ²	0.320	g/cm³	ASTM D1622

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw A ³	45	ASTM D2240
Shaw A ⁴	55	ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D412
Yield ⁵	1.17	MPa	ASTM D412
Yield ⁶	1.86	MPa	ASTM D412
Tensile Elongation ⁷(Break)	130	%	ASTM D412
Tear Strength			ASTM D624
--	4.03	kN/m	ASTM D624
--	5.78	kN/m	ASTM D624
Cracking ⁸	1.6	kN/m	ASTM D624
Cracking ⁹	2.1	kN/m	ASTM D624
Compression Set			ASTM D395B
70°C, 22 hr ¹⁰	15	%	ASTM D395B
70°C, 22 hr ¹¹	10	%	ASTM D395B

Flammability	Nominal Value	Unit	Test Method
Burning Rate			FMVSS 302
-- ¹²	0.0	mm/min	FMVSS 302
-- ¹³	0.0	mm/min	FMVSS 302

Additional Information
Processing parameters: Mix Ratio (Resin/Isocyanate): 100/38 pbw Isocyanate Temperature: 75 to 95°F Resin Temperature: 75 to 90°F Mold Temperature: 75 to 110°F Demold Time: 5 to 6 min Liquid Component: Density, Resin at 25°C, ASTM D1638: 1.05 g/cm³ Density, Isocyanate at 25°C, ASTM D1638: 1.20 g/cm³ Viscosity, Resin at 25°C, ASTM D2196: 500 cP Viscosity, Isocyanate at 25°C, ASTM D2196: 150 cP Hand Mix at 77°F: Cream Time: 20 sec Top of Cup: 50 sec Gel Time: 70 sec Rise Time: 110 sec Tack Free Time: 130 sec Free Rrise Density: 7.0 lb/ft³ High Pressure at 77°F: Cream Time: 13 sec Top of Cup: 35 sec Gel Time: 50 sec Rise Time: 75 sec Tack Free Time: 100 sec Free Rrise Density: 6.5 lb/ft³

Additional Information

Processing parameters: Mix Ratio (Resin/Isocyanate): 100/38 pbw Isocyanate Temperature: 75 to 95°F Resin Temperature: 75 to 90°F Mold Temperature: 75 to 110°F Demold Time: 5 to 6 min Liquid Component: Density, Resin at 25°C, ASTM D1638: 1.05 g/cm³ Density, Isocyanate at 25°C, ASTM D1638: 1.20 g/cm³ Viscosity, Resin at 25°C, ASTM D2196: 500 cP Viscosity, Isocyanate at 25°C, ASTM D2196: 150 cP Hand Mix at 77°F: Cream Time: 20 sec Top of Cup: 50 sec Gel Time: 70 sec Rise Time: 110 sec Tack Free Time: 130 sec Free Rrise Density: 7.0 lb/ft³ High Pressure at 77°F: Cream Time: 13 sec Top of Cup: 35 sec Gel Time: 50 sec Rise Time: 75 sec Tack Free Time: 100 sec Free Rrise Density: 6.5 lb/ft³

Note Message
1 .	Hand Mix
2 .	High Pressure
3 .	Hand Mix
4 .	High Pressure
5 .	Hand Mix
6 .	High Pressure
7 .	Hand Mix
8 .	Hand Mix
9 .	High Pressure
10 .	Hand Mix
11 .	High Pressure
12 .	Hand Mix
13 .	High Pressure

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	BASF Corporation
Trademark:	Elastofoam®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cQZad3_Elastofoam38100R3120T.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Tufpet PBT SX1040	Mitsubishi Rayon America Inc.	PBT	Tufpet
KPOL-LLDPE LLD K-21/927	KPOL Chem Co.	LLDPE	KPOL-LLDPE
LITEN BB 10	UNIPETROL RPA	PE Copolymer	LITEN
LNP™ LUBRICOMP™ LL002 compound	SABIC Innovative Plastics	PEEK	LNP™ LUBRICOMP™
MAJORIS HPS G400 - 8229	AD majoris	PPS	MAJORIS