QR Resin QR-1000-GF40
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cPv1hi_QR-Resin-QR-1000-GF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available with UV (V) or Release (R). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 159 | MPa | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 183 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 154 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-901-D | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Geon™ Vinyl Cellular E2500 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Cellular |
| EPO-TEK® H31 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Pibiter® NRV230AE NAT001 | SO.F.TER. SPA | PBT | Pibiter® |
| Polygen SC75C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |