VALOX™ V9561 resin
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cPMiRz_VALOX-V9561-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/5.0 kg | 30 | g/10 min | |
| 266°C/5.0 kg | 30 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 33.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.30 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.050 | % | |
| Equilibrium, 23°C, 50% RH | 0.25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 265 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 13000 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 145 | MPa | ASTM D638 |
| Yield | 143 | MPa | ISO 527-2/5 |
| Break 4 | 145 | MPa | ASTM D638 |
| Break | 143 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 2.2 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 6 | 2.2 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 7 | 10800 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Flexural Strain at Break 8 | 2.3 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 36 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 6.0 | kJ/m² | ISO 179/2C |
| 23°C 9 | 7.0 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 0°C | 60 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 0°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 430 | J/m | ASTM D4812 |
| 23°C | 550 | J/m | ASTM D4812 |
| -30°C 13 | 35 | kJ/m² | ISO 180/1U |
| 23°C 14 | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 15 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 245 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 200 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 255 | °C | ASTM D1525, ISO 306/A50 12 16 |
| -- | 235 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 17 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.9E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 6.7E-5 | cm/cm/°C | |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| 3.00 mm | 800 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 260 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 90.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | Rate A (50°C/h), Loading 2 (50 N) |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PurSil™ 20 80A | DSM Biomedical Inc. | TPU, Unspecified | PurSil™ |
| Ultradur® B 2300 G6 HR LS BK15045 | BASF Corporation | PBT | Ultradur® |
| DURAFIDE® 1130A64 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| LNP™ THERMOCOMP™ UFW49RSC compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| Eleme NGL045RG | Eleme Petrochemical Company Ltd | MDPE | Eleme |