Plexiglas® Resist zk50

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cNsRNl_Plexiglas-Resist-zk50.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Resist zk50 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk50 is characterized by the following special properties:

maximum break resistance and impact strength

improved resistance to stress cracking

certified dishwasher resistance

Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.

Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware

General Information
Additive	Impact Modifier
Features	High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Appliances Flexible Grips Household Goods Profiles Sanitary Products Writing Instruments
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.12	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	0.100	cm³/10min	ISO 1133
Water Absorption (Equilibrium, 23°C, 50% RH)	0.42	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	950	MPa	ISO 527-2/1
Tensile Stress (Yield)	25.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	%	ISO 527-2/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	13	kJ/m²	ISO 179/1
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	73.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	70.0	°C	ISO 75-2/A
Glass Transition Temperature	115	°C	ISO 11357-2
Vicat Softening Temperature	75.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	1.5E-4	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	89.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	< 65.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	230 to 240	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Star L PA66 30V D51	Eurostar Engineering Plastics	Nylon 66	Star L
VESTAMID® L X7293	Evonik Industries AG	Nylon 12	VESTAMID® L
Karina BLACK COLOR CONCENTRATE MBU -E 48/ 1-IE	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ VERTON™ MV006SU compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ VERTON™
TechnoElast S A8008 I 1 nat	TechnoCompound GmbH	TPE	TechnoElast