Witcom PP H/2C
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cNPiRy_Witcom-PP-H-2C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PP H/2C is a Polypropylene Homopolymer (PP Homopolymer) product filled with 10% carbon fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 to 1.0 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.040 | % | |
| Equilibrium, 23°C, 50% RH | 0.010 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 to 5.0 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 201FG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Addisil™ 2050 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| apinat® A 65 | API SpA | TPE | apinat® |
| LEXAN™ FST9436 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina CLEAR PVC COMP. -E 87/206-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |