| Envir® PA6N3L-BK0305 is a General Purpose Nylon 6 molding resin. 6N3L is Nucleated and Lubricated for fast molding cycle times and easy processing. It is provided Black in color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 20.0 | cm³/10min | ASTM D1238 |
| Ash Content | < 0.50 | % | ASTM D5630 |
| Moisture Content | < 0.20 | % | ASTM D6980 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Granularity | 1.50 | g/100 pellets |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 78.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | 17 | % | |
| Flexural Modulus | 3030 | MPa | ISO 178 |
| Flexural Stress | 113 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT40-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| DOW™ HDPE 82054T | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Geon™ Vinyl Rigid Extrusion 87547 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| HiFill® PA6/6 GB15 | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Mafill® CR C 1044 | Ravago Group | PP Homopolymer | Mafill® |