UmaPET WHLO Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
KEY FEATURES UmaPET WHLO is one side chemically primed white opaque film. It has high opacity and high whiteness. Chemically coated surface provides enhanced adhesion to inks and coatings. Shows excellent flatness, good dimensional stability at elevated temperatures and exhibits excellent processability. APPLICATIONS Self adhesive label face stocks, lidding in high end applications, promotional calendars, Tickets for multiple uses, Prepaid cards, security and access cards, ink jet printing film, Photographic printing, high quality replacement for paper as a backing in blister packs, stationary and other industrial and packaging applications.

General Information
Features	Good Adhesion Good Dimensional Stability Good Processability
Uses	Film Labels Stationary Supplies
Appearance	Opaque
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0300 mm	2.5	%
Flow : 150°C, 30 min, 0.0360 mm	2.5	%
Flow : 150°C, 30 min, 0.0500 mm	2.0	%
Across Flow : 150°C, 30 min, 0.0300 mm	0.60	%
Across Flow : 150°C, 30 min, 0.0360 mm	0.60	%
Across Flow : 150°C, 30 min, 0.0500 mm	0.60	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.40
vs. Itself - Dynamic ²	0.40
vs. Itself - Dynamic ³	0.40
vs. Itself - Static ⁴	0.50
vs. Itself - Static ⁵	0.50
vs. Itself - Static ⁶	0.50

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	30 36 50	µm
Film Thickness - Recommended / Available	30, 36, 50 µm
Tensile Strength			ASTM D882
MD : Break, 30 µm	167	MPa
MD : Break, 36 µm	157	MPa
MD : Break, 50 µm	157	MPa
TD : Break, 30 µm	177	MPa
TD : Break, 36 µm	167	MPa
TD : Break, 50 µm	167	MPa
Tensile Elongation			ASTM D882
MD : Break, 30 µm	120	%
MD : Break, 36 µm	120	%
MD : Break, 50 µm	120	%
TD : Break, 30 µm	80	%
TD : Break, 36 µm	80	%
TD : Break, 50 µm	80	%
Yield			Internal Method
30.0 µm	23.8	m²/kg
36.0 µm	19.8	m²/kg
50.0 µm	14.1	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Coated side : 30.0 µm	48	dyne/cm
Coated side : 36.0 µm	48	dyne/cm
Coated side : 50.0 µm	48	dyne/cm
Plain side : 30.0 µm	42	dyne/cm
Plain side : 36.0 µm	42	dyne/cm
Plain side : 50.0 µm	42	dyne/cm

Optical	Nominal Value	Unit	Test Method
Opacity			Internal Method
-- ⁷	88	%
-- ⁸	90	%
-- ⁹	90	%
Haze			ASTM D1003
30.0 µm	98	%
36.0 µm	98	%
50.0 µm	98	%

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cMWLhg_UmaPET-WHLO.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 4081 AR 10 TFE 20 SI 2	RTP Company	PPA	RTP
Shinko-Lac® ASA TW10	Mitsubishi Rayon America Inc.	ASA	Shinko-Lac®
Sultron® R60	Asia International Enterprise (Hong Kong) Limited	PPS	Sultron®
Veromor® Purge -XT	PlastxWorld Inc.	Proprietary	Veromor® Purge
Osterlene® PPC-.75-NB	Osterman & Company	PP Impact Copolymer	Osterlene®