SABIC® STAMAX 30YK270
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLyR3Q_SABIC-STAMAX-30YK270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 30YK270 is a 30% long glass fiber reinforced grade with improved impact and flow properties. The glass fibres are chemically coupled to the PP matrix, resulting in high stiffness and strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1B | ||
| 23°C, Injection Molded | 6200 | MPa | |
| 80°C, Injection Molded | 4400 | MPa | |
| 120°C, Injection Molded | 3600 | MPa | |
| Tensile Stress 1 | ISO 527-2 | ||
| 23°C, Injection Molded | 98.0 | MPa | |
| 80°C, Injection Molded | 60.0 | MPa | |
| 120°C, Injection Molded | 43.0 | MPa | |
| Tensile Strain (Break, 23°C, Injection Molded) | 2.3 | % | ISO 527-2/1B |
| Flexural Modulus | ISO 178 | ||
| 23°C, Injection Molded | 5500 | MPa | |
| 80°C, Injection Molded | 3600 | MPa | |
| Flexural Stress | ISO 178 | ||
| 23°C, Injection Molded | 138 | MPa | |
| 80°C, Injection Molded | 70.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Injection Molded | 24 | kJ/m² | |
| 23°C, Injection Molded | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Injection Molded | 70 | kJ/m² | |
| 23°C, Injection Molded | 57 | kJ/m² | |
| Falling Dart Impact - Total Energy 2(23°C) | 58.0 | J/cm | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 157 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.4E-5 | cm/cm/°C | |
| 23 to 80°C | 3.7E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Type 1B |
| 2 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® HT NT40 NL XA60 | Eurotec Engineering Plastics | PPA | Tecomid® HT |
| Utomer UT380 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| DESOX™ DSC410I | DESCO Co., Ltd. | PBT | DESOX™ |
| Petrothene® GA818073 | LyondellBasell Industries | LLDPE | Petrothene® |
| Hifax TYC 900P C11301 | LyondellBasell Industries | PP, Unspecified | Hifax |