Plenco 02369 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLuY1P_Plenco-02369-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369 offers excellent physical and electrical strength properties. UL recognized under component file E40654. 02369 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.66 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.62 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 72 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7350 | MPa | ASTM D638 |
| Tensile Strength | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 6900 | MPa | ASTM D790 |
| Flexural Strength | 86.7 | MPa | ASTM D790 |
| Compressive Strength | 188 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18.9 | J/m | ASTM D256 |
| Notched Izod Impact | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 176 | °C | ASTM D648 |
| Continuous Use Temperature | 184 | °C | ASTM D794 |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 9.4 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 6.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.056 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.52%Heat Resistance, ASTM D794: 184°CDrop Ball Impact, PLENCO Method: 107 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 G3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Ultramid® 8233G HS | BASF Corporation | Nylon 6 | Ultramid® |
| Yanshan PE 1130A | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Multiuse Leostomer® LE-3190N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| FHR Polypropylene P9R6K-054A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |