Hostacom TKC 270N D72253
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLN08C_Hostacom-TKC-270N-D72253.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom TKC 270N is a 14% mineral filled polypropylene copolymer for injection moulding. It combines good processability with excellent stiffness/ impact properties, and offers good scratch resistance. The grade has been specifically designed for automotive interior trim applications. Basell Color D72253 is a color-matched variant of this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 19.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant (23°C) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 3.5 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 51.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® V143XL | Celanese Corporation | LCP | VECTRA® |
| WPP PP PPH3CF3.5-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| DURANEX® 353RA | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Hifax EKF 212 D | LyondellBasell Industries | PP, Unspecified | Hifax |
| LEXAN™ LUX2614G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |