SABIC® PP 86MF97
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cLGY1T_SABIC-PP-86MF97.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 86MF97 is a grade which is characterised by an optimum combination of stiffness, impact resistance and flow. It is highly UV-stabilised, and therefore commonly used for exterior applications such as car bumpers. SABIC® PP 86MF97 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.6 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 24 hr | 1.6 | % | |
| 24 hr | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 1050 | MPa | ASTM D638 |
| Injection Molded | 1000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, Injection Molded) | 22.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, Injection Molded) | 6.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break | ||
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C, Injection Molded | 85 | J/m | ASTM D256A |
| 0°C, Injection Molded | No Break | ASTM D256A | |
| 23°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| -20°C, Injection Molded | 8.0 | kJ/m² | ISO 180/1A |
| 0°C, Injection Molded | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/A120 4 2 |
| -- | 62.0 | °C | ASTM D1525, ISO 306/B120 5 3 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 TFE 10 | RTP Company | PPA | RTP |
| Radilon® S 38F 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| TPV Elastoprene® N87A-S | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Nypol® PA B3 HF BRC0003 NT336 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| DJSilicone NE-- T-1/NE-T-1U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |