PLUSTEK PA517
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cIlhD0_PLUSTEK-PA517.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen Free Polyamide 6.6/6. Formulated to meet V-0 UL-94 , for Injection Moulding application. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.0 - 1.4 | % | ASTM D955 |
| -- | 1.0 - 1.4 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 7.5 | % | ASTM D570 |
| Saturated, 23°C | 7.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 130 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 180 | °C | |
| Maximum Continuous Use Temperature | 80 | °C | |
| Melting Temperature | 250 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 70 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech T9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| Sylvin 9077-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| KOCETAL® K500 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Iupilon® H-4000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LUBAN™ 1100 N | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |