Vamac® VMX-2122
| Category: | AEM , Ethylene Acrylic Elastomer |
| Manufacturer: | DuPont Performance Elastomers |
| Trademark: | Vamac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cIN7Ys_VamacVMX2122.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vamac® ethylene acrylic elastomer, introduced in 1975, has been successfully used for many years in demanding automotive applications, where excellent resistance to heat, engine and transmission fluids or Blow-By is required. DuPont's latest manufacturing technology allows production of enhanced AEM grades that are significantly improved compared to the existing standard Vamac® elastomers. These grades, designated and sold as Vamac® Ultra, provide a true step-change improvement in processability, performance and customer value for targeted applications. The new manufacturing technology has now also been applied to a new EMA Dipolymer, called VMX-2122. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 18 - 34 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shao A, 1 second, 6.00mm) | 79 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 7.00 | MPa | ASTM D412 |
| Tensile Stress (Break) | 11.5 | MPa | ISO 37 |
| Tensile Elongation (Break) | 270 | % | ASTM D412 |
| Tear Strength | ISO 34-1 | ||
| -- 2 | 6.5 | kN/m | ISO 34-1 |
| -- 3 | 38 | kN/m | ISO 34-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| 100°C, 168 hr | 7.0 | % | ASTM D573 |
| 100% strain, 160°C, 168 hr | 22 | % | ASTM D573 |
| 175°C, 168 hr | 2.0 | % | ASTM D573 |
| 100% strain, 175°C, 168 hr | 33 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 160°C, 168 hr | -10 | % | ASTM D573 |
| 175°C, 168 hr | -31 | % | ASTM D573 |
| Change in Durometer Hardness in Air | ASTM D573 | ||
| Shao A, 160°C, 168 hr | 4.0 | ASTM D573 | |
| Shao A, 175°C, 168 hr | 5.0 | ASTM D573 | |
| Change in Tensile Strength | ASTM D471 | ||
| 100°C, 168 hr, in IRM 903 oil | 3.0 | % | ASTM D471 |
| 100% strain, 100°C, 168 hr, in IRT 903 oil | 2.9 | % | ASTM D471 |
| Change in Ultimate Elongation (100°C, 168 hr, in IRM 903 oil) | -32 | % | ASTM D471 |
| Change in Durometer Hardness (Support A, 100°C, 168 hr, in IRM 903 oil) | -13 | ASTM D471 | |
| Change in Mass (100°C, 168 hr, in IRM 903 oil) | 16 | % | ASTM D471 |
| Change in Volume (100°C, 168 hr, in IRM 903 oil) | 27 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 4 | -27.8 | °C | ASTM E1356 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volatiles | wt% | Internal method |
| Note Message | |
|---|---|
| 1 . | Plied |
| 2 . | Method A, Pant-Shaped Specimen |
| 3 . | Method B, right-angle specimen (without cut) |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast NP BF 001 | NaturePlast | Biodeg Polymers | NaturePlast |
| ALCOM® PP 620/1 MR40 WT1060-12LB | ALBIS PLASTIC GmbH | PP, Unspecified | ALCOM® PP |
| APEX® 2085-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Huafon EP158N | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| IPC PP 4810C-T | International Polymers Corporation | PP Copolymer | IPC PP |