Lucky Enpla LAY1000
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cI4aNC_Lucky-Enpla-LAY1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LAY1000 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Lucky Enpla LAY1000 applications include electrical/electronic applications, housing and automotive industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 54.9 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2110 | MPa | ASTM D790 |
| Flexural Strength 3 | 77.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 800-1200 kg/cm²Injection Pressure (2nd Pressure): 300-700 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® MDFS2 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Kynar® 740 Black | Arkema | PVDF | Kynar® |
| Jam HDPE HH4765 | Jam Petrochemical Company | HDPE | Jam HDPE |
| LG ABS MP220 | LG Chem Ltd. | ABS | LG ABS |
| LNP™ THERMOCOMP™ CF008 compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ THERMOCOMP™ |