LNP™ LUBRICOMP™ ZL003 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cHmkOU_LNPLUBRICOMPZL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features of this material include:internally Lubricated. Also known as LUBRICOMP ZL-4030 Also known as: LNP* LUBRICOMP* Compound ZL-4030 Product Reorder name: ZL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.87 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.83 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Fracture | 46.9 | MPa | ASTM D638 |
| Fracture 3 | 46.0 | MPa | ASTM D638 |
| Fracture | 46.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 8.5 | % | ASTM D638 |
| Yield 4 | 8.5 | % | ASTM D638 |
| Yield | 8.1 | % | ISO 527-2, ISO 527-2/5 |
| Fracture | 8.9 | % | ASTM D638 |
| Fracture 5 | 8.9 | % | ASTM D638 |
| Fracture | 8.3 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2750 | MPa | ASTM D790 |
| -- | 2760 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| -- 7 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 75.0 | MPa | ISO 178 |
| -- | 75.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 75.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.28 | ASTM D3702 Modified | |
| With Self-Static | 0.20 | ASTM D3702 Modified | |
| Wear Factor - Washer | 11.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 9 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 10 | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 11 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 117 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 119 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 - 288 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 299 - 310 | °C | |
| Processing (Melt) Temp | 299 - 304 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 3696/25 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| SMOKEGUARD™ O 404 NATURAL | AlphaGary | Polyolefin, Unspecified | SMOKEGUARD™ O |
| Axiall PVC 11701 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Clariant Nylon 6/6 6601-L BK-09 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Sylvin 9770-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |