AZDEL™ PM10400
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cHLgr7_AZDEL-PM10400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL PM10400 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a generally homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6160 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 5600 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Compressive Strength | 138 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 16.3 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 21.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 154 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 2.5 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.9 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 40 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 750 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 750 J/mPoissons Ratio, ISO 527: 0.35Sheet Thickness, Internal Test Method: 146 milsSpecific Gravity, ASTM D792, Laminated: 1.18Specific Gravity, ASTM D792, Molded: 1.21 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® NB1803E-BK | Wellman Engineering Resins | Nylon+PP | Wellamid® |
| LNP鈩?THERMOCOMP鈩?OF008G compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| OP - PPS 30GF-15PTFE | Oxford Polymers | PPS | OP - PPS |
| Sumiliteresin® PR-53365 | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 9077-75 Yellow 4181 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |