Low Density Polyethylene (LDPE)

Typical applications include toys, lids, and closures

Good gloss, rigidity, excellent flow

Complies with U.S. FDA 21 CFR 177.152 (c) 2.1

Complies with Canadian HPFB No Objection (With Limitations)

Complies with EU, No 10/2011

Consult the regulations for complete details

DOW Polyethylene 993I Low Density Polyethylene Resin is a medium molecular weight distribution homopolymer designed to offer good gloss and rigidity with excellent flow characteristics. This resin has good processability over a wide range of molding conditions.

General Information
Additive	Sliding agent (400 ppm)
Agency Ratings	FDA 21 CFR 177.1520(c) 2.1 HPFB (Canada) No Objection 2 Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.923	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	25	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50)	< 1.00	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	43		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	10.3	MPa	ASTM D638
Fracture	11.7	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	3.0	%	ASTM D638
Fracture	40	%	ASTM D638
Flexural Modulus - 2% Secant	317	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	420	J/m	ASTM D256
Tensile Impact Strength ¹	252	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	40.0	°C	ASTM D648
Brittleness Temperature	-33.9	°C	ASTM D746
Vicat Softening Temperature	92.8	°C	ASTM D1525
Melting Temperature (DSC)	110	°C	Internal method
Peak Crystallization Temperature (DSC)	100	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Note Message
1 .	Type s

Resin Grade	Manufacturer	Category	Trademark
RTP 199 X 138789 EG	RTP Company	PP, Unspecified	RTP
Yanshan PE 5200B	SINOPEC Beijing Yanshan Petrochemical	HDPE	Yanshan PE
Daelim Po1y® PH-470	DAELIM INDUSTRIAL CO., LTD.	PP Homopolymer	Daelim Po1y®
EL-Lene™ H5818J	SCG Chemicals Co., Ltd.	HDPE	EL-Lene™
Capilene® QC 71 E	Carmel Olefins Ltd.	PP Random Copolymer	Capilene®