GAPEX® RPP30EB01HB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cGQGDS_GAPEX-RPP30EB01HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX® RPP30EB01HB is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of GAPEX® RPP30EB01HB are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.7 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant | 5580 | MPa | |
| Tangent | 5710 | MPa | |
| Flexural Strength (23°C) | 129 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Gardner Impact | 0.339 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 147 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 221 to 238 | °C | |
| Middle Temperature | 227 to 243 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Nozzle Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 221 to 238 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 to 0.345 | MPa | |
| Cushion | 5.08 to 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILITE AC3800 | Formosa Plastics Corporation | PC | TAIRILITE |
| Vinnolit® E 75 HV | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Boda BDF-LG2752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EVICOM™ GA4/130 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| EPO-TEK® H35-175MPT | Epoxy Technology Inc. | Epoxy | EPO-TEK® |