Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber, 60% filler by weight
Features	Thermal Stability
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.70	g/cm³	ISO 1183
Molding Shrinkage ¹	0.30	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	22500	MPa	ISO 527-2
Tensile Stress (Break)	270	MPa	ISO 527-2
Tensile Strain (Break)	1.5	%	ISO 527-2
Flexural Modulus	19500	MPa	ISO 178
Flexural Stress	420	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	20	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	90	kJ/m²	ISO 179
Dart Drop Impact	13.1	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	280	°C	ISO 75-2/A
8.0 MPa, not annealed	237	°C	ISO 75-2/C

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Processing (Melt) Temp	290 - 320	°C
Mold Temperature	140	°C
Injection Rate	Slow-Moderate
Back Pressure	1.00	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Note Message
1 .	Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions.

Resin Grade	Manufacturer	Category	Trademark
RAMOFIN PPH300J8	Polyram Ram-On Industries	PP Homopolymer	RAMOFIN
TAIRIPRO B8001	Formosa Plastics Corporation	PP Impact Copolymer	TAIRIPRO
Adell Polyamide BR-710	Adell Plastics, Inc.	Nylon 6	Adell Polyamide
Electrafil® ABS SS15 BK MB	Techmer Engineered Solutions	ABS	Electrafil®
EnviroTPO 2010T20	West Michigan Compounding	Polyolefin, Unspecified	EnviroTPO