| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cGF59q_DynaStat-1857.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Static Dissipative Acetal Compound Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 43.4 | MPa | ASTM D638 |
| Fracture | 34.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 17 | % | ASTM D638 |
| Fracture | > 100 | % | ASTM D638 |
| Flexural Modulus | 1480 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 292 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 - 1.0E+9 | ohms | ASTM D257 |
| Static Decay | sec | NFPA 99 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 191 - 199 | °C | |
| Middle Temperature | 196 - 202 | °C | |
| Front Temperature | 199 - 204 | °C | |
| Nozzle Temperature | 202 - 207 | °C | |
| Processing (Melt) Temp | 204 - 210 | °C | |
| Mold Temperature | 37.8 - 82.2 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 193 | °C | |
| Cylinder Zone 3 Temp. | 188 - 199 | °C | |
| Cylinder Zone 5 Temp. | 193 - 204 | °C | |
| Melt Temperature | 199 - 210 | °C | |
| Die Temperature | 193 - 204 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 25 to 100 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® G3500HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Lupoy® SC1004A | LG Chem Ltd. | PC | Lupoy® |
| Polifil® PP T-10 | The Plastics Group | PP Homopolymer | Polifil® PP |
| Honghai CPE 130A | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |
| VALOX™ 771 resin | SABIC Innovative Plastics | PBT | VALOX™ |