Riteflex® XFR 655
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Riteflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cFyVp0_Riteflex-XFR-655.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Riteflex XFR 655 is a thermoplastic polyester elastomer featuring a halogen-free flame retardant system and is UL certified to be V-0 at 1.5 mm in all colors. It has shore D hardness of 55 and an excellent balance of mechanical properties, flame retardant efficiency and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.7 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 360 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Fracture | 16.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 14.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 250 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength - Flow 1 | 55 | kN/m | ISO 34-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 2 | 200 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 200 - 215 | °C | |
| Middle Temperature | 215 - 230 | °C | |
| Front Temperature | 215 - 230 | °C | |
| Nozzle Temperature | 215 - 235 | °C | |
| Processing (Melt) Temp | 220 - 235 | °C | |
| Mold Temperature | 20.0 - 55.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 215 to 235°CScrew Speed: Medium |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P4-30FG-0522 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Unilex™ UP 8034 | United Polychem | PP Homopolymer | Unilex™ |
| 陶氏低密度聚乙烯 615C | The Dow Chemical Company | LDPE | DOW™ LDPE |
| Kepital® F20-03 BBK | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| POLYelast TPE ED80 D40 UV | Polykemi AB | PP+EPDM | POLYelast |