PRL PPX-FR1-(color)-EN
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cELBoN_PRL-PPX-FR1--color--EN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-FR1-(color)-EN is a polyphenylene ether PS (PPE PS) product,. It can be processed by extrusion and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 15 - 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18mm | 56.5 | MPa | ASTM D638 |
| Fracture, 3.18mm | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2280 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 370 | J/m | ASTM D256 |
| Dart Drop Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 87.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 82.2 | °C | ASTM D648 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 110 | °C | UL 746 |
| 1.70 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 95.0 | °C | UL 746 |
| 1.70 mm | 95.0 | °C | UL 746 |
| 3.00 mm | 95.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 110 | °C | UL 746 |
| 1.70 mm | 110 | °C | UL 746 |
| 3.00 mm | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) (1.50 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 1 | UL 746 | |
| 1.70 mm | PLC 1 | UL 746 | |
| 3.00 mm | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (1.50 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 1.70 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | UL 94 | |
| 1.70 mm, ALL | V-0 | UL 94 | |
| 3.00 mm, ALL | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 171 | °C | |
| Cylinder Zone 2 Temp. | 188 | °C | |
| Cylinder Zone 3 Temp. | 188 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 204 | °C |
| Extrusion instructions |
|---|
| Do not exceed 8 hours when drying. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A90 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| S&E Battery GPP1005M-EX8 | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| MTM® 85S | Cytec Industries Inc. | Phenolic | MTM® |
| NEXUS PP CPP35/2 | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| OmniLon™ PA6/6 U GR23 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |