LNP™ VERTON™ RX89047 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cD2Cwh_LNP-VERTON-RX89047-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RX89047 is a compound based on Nylon 66 resin containing Proprietary Fillers. Added feature of this grade is: Structural. Also known as: LNP* VERTON* Compound PDX-R-89047 Product reorder name: RX89047 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.41 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11400 | MPa | ASTM D638 |
| Tensile Strength | |||
| Break | 202 | MPa | ASTM D638 |
| Break | 198 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.3 | % | ASTM D638 |
| Break | 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 9500 | MPa | ISO 178 |
| Flexural Strength | 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D256 |
| 23°C 2 | 24 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1000 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 251 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5230R B11 | Spartech Polycom | PP, Unspecified | Spartech |
| STARFLEX® P 7027-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| NuSil FS-3730-2 | NuSil Technology | Silicone | NuSil |
| Akulon® F127 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| ELASTOSIL® R 420/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |