Toyolac® 844V X05
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c9f5st_Toyolac-844V-X05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 844V X05 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 844V X05 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 35 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 41.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | > 5.0 | % | ASTM D638 |
| Break | > 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 2230 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 66.0 | MPa | ASTM D790 |
| -- 5 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 190 | J/m | |
| 23°C, 12.7 mm | 140 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 76.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 2.50 mm | 5VA |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® A AG6I | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| VAMPLEN 0024 V2 LBC | Vamp Tech | PP Homopolymer | VAMPLEN |
| GLS Nylon 66 LN06 | GLS Polymers Pvt. Ltd. | Nylon 66 | GLS Nylon 66 |
| Hostacom EKC 330N E1 C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |
| POCAN® ECO T 3230 000000 | LANXESS Corporation | PBT+PET | POCAN® |