TIPELIN® FA 381-10
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c9Il4r_TIPELIN-FA-381-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN FA 381-10 is a film grade of medium density polyethylene copolymer (with hexen-1 as comonomer) grade. The product has very good Elmendorf tear strength and Dart drop resistance, low gel content and good vapour barrier capacity. The grade contains antioxidants and acid scavenger. Applications TIPELIN FA 381-10 is recommended for bags, shopping bags, garbage bags, shrink films, multi-layer films and blend component for LDPE. TIPELIN FA 381-10 is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | |
| 190°C/21.6 kg | 21 | g/10 min | |
| 190°C/5.0 kg | 1.2 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 900 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 21.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 18.0 | MPa | |
| MD : 25 µm, Blown Film | 48.0 | MPa | |
| TD : 25 µm, Blown Film | 47.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 700 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 100 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm, Blown Film | 0.49 | N | |
| TD : 25 µm, Blown Film | 4.0 | N | |
| Spencer Impact - Blown Film (25.0 µm) | 35.0 | MPa | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | 32 | min | EN 728 |
| Vicat Softening Temperature | 118 | °C | ISO 306/A120 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6300HH | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| TES J-80/20 | Techmer Engineered Solutions | Acetal (POM) Copolymer | TES |
| Hyundai EP PA6 LS285 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Panlite® K-1285ZH | TEIJIN LIMITED | PC | Panlite® |
| KOPA® KN173ST | Kolon Plastics, Inc. | Nylon 6 | KOPA® |