| Polyaryletherketone, Wear Grade, with Tg of 320 °F (160 °C) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 9500 | MPa | ASTM D790 |
| Flexural Strength | 234 | MPa | ASTM D790 |
| Poisson's Ratio | 0.45 | ||
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.11 | ||
| Static | 0.11 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (0.318 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | ASTM D648 |
| Glass Transition Temperature | 182 | °C | ASTM E1356 |
| Melting Temperature | 350 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 380 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 200 to 210 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6895 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Hylon® N1000TH | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| PHOENIX™ 8554 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| SABIC® LDPE 2602H0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| SABIC® PPcompound 7450 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |