ENGAGE™ 8107
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c6bpsg_ENGAGE-8107.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™8107 polyolefin elastomer is an ethylene-octene copolymer with excellent flow properties and has a wide range of applications in general-purpose thermoplastic elastomers. After blending with polypropylene (PP) and polyethylene (PE), ENGAGE 8107 has particularly excellent impact resistance. ENGAGE 8107 has high filler content and excellent peroxide curing performance. After being cured by peroxide, silane and irradiation, the product has excellent thermal aging properties, compression deformation and weather resistance, and may be used in the manufacture of high-performance electrical insulation products. Main features:
Application field:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 24 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 73 | ASTM D2240 | |
| Shore D, 1 second, molded | 22 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.90 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 9.76 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 810 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 14.3 | MPa | ASTM D790 |
| 2% secant : Molding | 13.1 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 40.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal method |
| Vicat Softening Temperature | 45.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 60.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 45.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 520 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Manner Flexible PVC X3687 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Ravathane R210A85UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| RTP 101 HI HF | RTP Company | PP Copolymer | RTP |
| Monprene® SP-13433 | Teknor Apex Company | TPE | Monprene® |