ABSCOM® S105
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Compounders Limited |
| Trademark: | ABSCOM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c4TaRS_ABSCOM-S105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABSCOM S105 is an easy flowing injection moulding general purpose ABS grade with exceptional colour performance. Typical applications include white goods, automotive, electronics and point of sale devices. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.22 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Yield, -40°C | 63.0 | MPa | ISO 527-2 |
| Yield, 80°C | 19.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 2.6 | % | ISO 527-2/50 |
| Yield, -40°C | 3.6 | % | ISO 527-2 |
| Yield, 80°C | 2.4 | % | ISO 527-2 |
| Break | 10 | % | ISO 527-2 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 180 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.5E-6 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 60 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VeroBlue™ RGD840 | Stratasys | Unspecified | VeroBlue™ |
| BESTNYL SC00VI02AH15 | Triesa Plastics | Nylon 66/6 | BESTNYL |
| Geon™ Vinyl Flexible R277AM | PolyOne Corporation | PVC+NBR | Geon™ Vinyl Flexible |
| Grivory® XE 4217 black 9233 | EMS-GRIVORY | Nylon 6T/66 | Grivory® |
| KOPEL® KP3363 | Kolon Plastics, Inc. | TPEE | KOPEL® |