Makroblend® AR205
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c3o2gP_Makroblend-AR205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PET) blend, easy flow, impact modified; application: automotive body panels |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 270°C, 3.00 mm | 0.70 to 0.90 | % | |
| Flow : 270°C, 3.00 mm | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 54.0 | MPa | |
| Break, 23°C | 48.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 4.8 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| 23°C | 80.0 | MPa | |
| 3.5% Strain, 23°C | 68.0 | MPa | |
| Flexural Strain at Flexural Strength 4(23°C) | 5.8 | % | ISO 178 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 5(270°C) | 200 | Pa·s | ISO 11443-A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | |||
| -30°C | 20 | kJ/m² | ISO 180/A |
| -30°C | No Break | ISO 180/1C | |
| 23°C | 45 | kJ/m² | ISO 180/A |
| 23°C | No Break | ISO 180/1C | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 48.0 | J | |
| 23°C | 42.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 5000 | N | |
| 23°C | 3900 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 126 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.1E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.2E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 70°C MT, 600 bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| 5 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 2003-BK | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| TECHNO ABS 600 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| BP RPP 3505 GM BLK | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| KOPLA ABS KSG1020F | KOPLA Co., Ltd. | ABS | KOPLA ABS |
| Paryls® PES F2250 GL20 | Youju New Materials Co., Ltd. | PESU | Paryls® |