Kotex KG-10MRA
| Category: | PC , Polycarbonate |
| Manufacturer: | Kotec Corporation |
| Trademark: | Kotex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c2L0bN_Kotex-KG-10MRA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kotex KG-10MRA is a Polycarbonate (PC) product filled with 10% glass fiber. It is available in Asia Pacific or Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 74.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3530 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | ASTM D150 | |
| Arc Resistance | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Haze (3.00 mm) | Translucent | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MP 181 | RASCHIG GmbH | Mel Phenolic | MELOPAS® |
| Unichem 8000 | Colorite Polymers | PVC, Unspecified | Unichem |
| INSTRUC FEPGF10 | Infinity LTL Engineered Compounds | FEP | INSTRUC |
| LIHAN® A9705P | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| LNP™ LUBRILOY™ RX99650 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |