RTP 205 D FR
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c12SEL_RTP-205-D-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Flame Retardant - UL94 V-0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12100 | MPa | ASTM D638 |
| Tensile Strength | 131 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 249 - 285 | °C | |
| Mold Temperature | 60.0 - 93.3 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7308FK | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| PrimaFlex® ABS 556 | Plastic Solutions, Inc. | ABS | PrimaFlex® |
| Borlink™ LE0595 | Borealis AG | XLPE | Borlink™ |
| Foam-It® 26 | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| LNP™ THERMOCOMP™ KF002XXP compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |