KetaSpire® KT-820 GF15 Datasheet,PEEK,Solvay Specialty Polymers-SHANGHAI SUSHENG

KetaSpire® KT-820 GF15

Category:	PEEK , Polyetheretherketone
Manufacturer:	Solvay Specialty Polymers
Trademark:	KetaSpire®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	c0rwiG_KetaSpire-KT-820-GF15.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
KetaSpire® KT-820 GF15 is a low flow, 15% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. The low fiberglass loading gives the resin improved surface aesthetics and reduced anisotropy over comparable 30% glass reinforced formulations. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in oil & gas, healthcare, transportation, electronics, chemical processing and other industrial uses. Natural: KT-820 GF15 NT

Message

KetaSpire® KT-820 GF15 is a low flow, 15% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. The low fiberglass loading gives the resin improved surface aesthetics and reduced anisotropy over comparable 30% glass reinforced formulations.

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.

These properties make it well-suited for applications in oil & gas, healthcare, transportation, electronics, chemical processing and other industrial uses.

Natural: KT-820 GF15 NT

General Information
Filler / Reinforcement	Glass Fiber, 15% Filler by Weight
Features	Autoclave Sterilizable Biocompatible E-beam Sterilizable Ethylene Oxide Sterilizable Fatigue Resistant Flame Retardant Good Chemical Resistance Good Dimensional Stability Good Sterilizability Heat Sterilizable High Flow High Heat Resistance High Stiffness High Strength Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable
Uses	Aircraft Applications Automotive Applications Connectors Dental Applications Electrical/Electronic Applications Film Hospital Goods Industrial Applications Medical Devices Medical/Healthcare Applications Oil/Gas Applications Pump Parts Seals Surgical Instruments
RoHS Compliance	Contact Manufacturer
Appearance	Tan
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.40	g/cm³	ASTM D792
Ash Content	15	%	ISO 3451-1

Mechanical	Nominal Value	Unit	Test Method
Modulus of Elasticity	6.10	GPa	ASTM D638
Tensile Modulus	6200	MPa	ASTM D638
Tensile Stress (Break)	124	MPa	ASTM D638
Tensile Strain ¹(Break)	5.0	%	ASTM D638
Flexural Stress	205	MPa	ASTM D638

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	9.5	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	85	kJ/m²	ISO 179
Notched Izod Impact Strength	9.0	kJ/m²	ISO 180
Unnotched Izod Impact Strength	74	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	218	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0	hr
Rear Temperature	365	°C
Middle Temperature	371	°C
Front Temperature	377	°C
Nozzle Temperature	382	°C
Mold Temperature	177 to 204	°C
Injection Rate	Fast
Screw Compression Ratio	2.5:1.0 to 3.5:1.0

Note Message
1 .	Type 1A, 5 mm/min

Resin Grade	Manufacturer	Category	Trademark
Pro-fax SV956	LyondellBasell Industries	PP Impact Copolymer	Pro-fax
Nylene® NX4747	Custom Resins Group	Nylon Copolymer	Nylene®
Cri-Line FKHT-717	Cri-Tech, Inc.	Fluorelastomer	Cri-Line
Latiohm 90/13-09 PD01 G/10	LATI S.p.A.	PPE+PS	Latiohm
Sumiliteresin® ECP-251	SBHPP	Epoxy	Sumiliteresin®

Resin Grade

Manufacturer