CALP GF2010A
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | CALP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c0hH7L_CALP-GF2010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALP GF2010A is a Polyolefin product filled with glass fiber. It can be processed by injection molding and is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 0.50 | % | |
| Across Flow : 2.00 mm | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 89.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 4200 | MPa | ASTM D790 |
| Flexural Strength | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 9.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 162 | °C | ASTM D648 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 2000-50A | Vi-Chem Corporation | TPE | Sevrene® |
| NEXT REGRIND PA6 8233-300RG | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REGRIND |
| Daelim Po1y® LD-61 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| Dynaprene® VE3080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Leona™ CR302 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |