Ultramid® Endure D3G7 BK20560
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c0LqPX_Ultramid-Endure-D3G7-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Endure D3G7 BK20560 is a glass fiber reinforced injection molding grade with high stiffness, very good flowability, and excellent heat aging resistance up to at least 220 degC (428 degF). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.87 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11300 | 7600 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 200 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.9 | 5.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10600 | 7400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 300 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | 14 | kJ/m² | |
| 23°C | 10 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| CLTE | ||||
| Flow | 1.4E-5 to 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 to 1.3E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 3.0E+14 | 4.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 48 | 29 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | 225 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2301R | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| TARODUR 100 G3 | Taro Plast S.p.A. | ABS | TARODUR |
| Abistir® UG GB/20 NATURALE | SO.F.TER. SPA | ABS | Abistir® |
| Sylvin 9048-80 Yellow 424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |