Clearflex® H&T CLH 156
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bz52S4_Clearflex-H-T-CLH-156.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T CLH 156 is a linear low density polyethylene resin, with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 156 show good optical properties, high puncture and dart resistance together with optimum performances in automatic wrapping machines (pre-stretch). Main Application Clearflex H&T CLH 156 is recommended to produce medium/high pre-stretch film. Moreover, the combination of high mechanical properties and low gel content, together with a low cling effect, makes Clearflex H&T CLH 156, even pure, the right choice in coextruded structures to produce high performance thin stretch film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 23 µm, Cast Film | 130 | MPa | |
| 1% Secant, TD : 23 µm, Cast Film | 140 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm, Cast Film | 10.0 | MPa | |
| TD : Yield, 23 µm, Cast Film | 10.0 | MPa | |
| MD : Break, 23 µm, Cast Film | 30.0 | MPa | |
| TD : Break, 23 µm, Cast Film | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm, Cast Film | 400 | % | |
| TD : Break, 23 µm, Cast Film | 600 | % | |
| Dart Drop Impact 1(23 µm, Cast Film) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 23.0 µm | 100.0 | kN/m | |
| TD : 23.0 µm | 150.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 91 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 1.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1843 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| BJB Polyurethane SP-301 A/B-4 | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Celcon® M270™ | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Escor™ 5110 | ExxonMobil Chemical | EAA | Escor™ |
| PLUSTEK RA300G3 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |