MALECCA K-300
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | MALECCA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bxbw6G_MALECCA-K-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MALECCA is a high heat resistant ABS resin which is based on styrene-N-phenylmaleimide copolymer. MALECCA was developed by Denka using their advanced polymerization technologies. This high heat ABS is much more highly improved in the areas of heat stability, processing characteristics and impact strength over traditional alpha-methylstyrene-based resins and is very easy to use. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.50 to 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 114 | ASTM D785 | |
| R-Scale | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 41.0 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 48.0 | MPa | |
| Break | 40.0 | MPa | |
| Nominal Tensile Strain at Break | 21 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2250 | MPa | ASTM D790 |
| -- 3 | 2450 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 75.0 | MPa | ASTM D790 |
| -- 5 | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16 | kJ/m² | ISO 179 |
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 120 | °C | ISO 306/B, ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ CRX1005 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Nymax™ GF1200 A13 BK010 ROHS | PolyOne Corporation | Nylon 66 | Nymax™ |
| Electrafil® HIPS C BK | Techmer Engineered Solutions | PS (HIPS) | Electrafil® |
| Hyundai EP Matt MF502L/Natural | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Matt |
| Osterlene® LLM1018 | Osterman & Company | LLDPE | Osterlene® |