Hostacom PPR 4142
| Category: | PP Homopolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bxEZ4M_Hostacom-PPR-4142.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" PPR 4142 is a unfilled polypropylene copolymer with good extraction resistance (hot water, steam). The product is designed for injection molding of dishwasher and washer parts exposed to hot water, steam and detergents and is available in natural color. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.8 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 6.60 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 58.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | > 6.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant (23°C) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | |
| 0°C | 4.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | > 50 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4185 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shin-Etsu Elastomer FEA-241U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Elastollan® C 60 AP | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| ENFLEX EA3555A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Petrothene® GA584189 | LyondellBasell Industries | LLDPE | Petrothene® |