LNP™ THERMOCOMP™ QF00A compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bwFLL2_LNPTHERMOCOMPQF00Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QF00A is a compound based on Nylon 6/10 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound QF-100-10 Product reorder name: QF00A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.7 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 10600 | MPa | ISO 178 |
| Flexural Stress | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 95 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 201 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.3E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYPROPYLENE 828-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Envirez® SS 70419 | Ashland Performance Materials | Polyester, TS | Envirez® |
| Karina CLEAR PVC COMPOUND -E 75/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ AT-10CF/5T BLACK | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| LEXAN™ 943X resin | SABIC Innovative Plastics | PC | LEXAN™ |