NORYL™ GFN1F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bu7Zly_NORYL-GFN1F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. 10% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 17 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 16.4 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | Internal Method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 104 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4350 | MPa | ASTM D638 |
| -- | 4400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 63.0 | MPa | ASTM D638 |
| Break | 64.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 3840 | MPa | ASTM D790 |
| 100 mm Span 4 | 3590 | MPa | ASTM D790 |
| -- | 4160 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 122 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 116 | MPa | ASTM D790 |
| Yield, 100 mm Span 6 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | 33 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| -30°C 8 | 9.4 | kJ/m² | ISO 180/1A |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| -30°C 10 | 25 | kJ/m² | ISO 180/1U |
| 23°C 11 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 21.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 12 | 132 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 124 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 131 | °C | ISO 306/B50 |
| -- | 134 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 5.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.4E-3 | ASTM D150 | |
| Arc Resistance 14 | PLC 7 | ASTM D495 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 5 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| 14 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylon® N3-25FG-2726 | Asahi Kasei Plastics North America Inc. | Nylon 66 | Thermylon® |
| Caltex PP M710H | GS Caltex | PP Impact Copolymer | Caltex PP |
| AVALON® 70 AE | Huntsman Corporation | TPU-Polyester | AVALON® |
| Cheng Yu PP228H | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Fainplast PVC RK 112 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |