VALOX™ K4530 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bt7UpW_VALOX-K4530-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.70 to 0.90 | % | |
| Across Flow : 3.20 mm | 1.0 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3560 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 103 | MPa | |
| Break 3 | 89.6 | MPa | |
| Break | 103 | MPa | |
| Break 4 | 82.0 | MPa | |
| Break 5 | 98.0 | MPa | |
| Tensile Elongation 6 | |||
| Yield | 4.0 | % | ASTM D638 |
| Yield 7 | 97 | % | ASTM D638 |
| Break 8 | 2.3 | % | ASTM D638 |
| Break | 4.0 | % | ASTM D638 |
| Break 9 | 2.5 | % | ASTM D638 |
| Flexural Modulus 10 | ASTM D790 | ||
| 50.0 mm Span 11 | 5100 | MPa | |
| 50.0 mm Span | 4640 | MPa | |
| 50.0 mm Span 12 | 4530 | MPa | |
| 50.0 mm Span 13 | 4820 | MPa | |
| Flexural Strength 14(Break, 50.0 mm Span) | 150 | MPa | ASTM D790 |
| Flexural Strain - 1.3 mm/min, 50 mm span | ASTM D790 | ||
| -- 15 | 7.0 | % | |
| -- 16 | 3.8 | % | |
| -- 17 | 9.7 | % | |
| -- 18 | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 58 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 400 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, Total Energy 19 | 5.30 | J | |
| 23°C, Total Energy 20 | 4.97 | J | |
| 23°C, Total Energy 21 | 6.10 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 193 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 76.7 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 4 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| 5 . | PROPERTIES AFTER 1008 HOURS AT 125°C |
| 6 . | Type I, 5.0 mm/min |
| 7 . | PROPERTIES AFTER 1008 HOURS AT 155°C |
| 8 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 9 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| 10 . | 1.3 mm/min |
| 11 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 12 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| 13 . | PROPERTIES AFTER 1008 HOURS AT 125°C |
| 14 . | 1.3 mm/min |
| 15 . | PROPERTIES AFTER 1008 HOURS AT 125°C |
| 16 . | PROPERTIES AFTER 1008 HOURS AT 155°C |
| 17 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| 18 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 19 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
| 20 . | PROPERTIES AFTER 1008 HOURS AT 125°C |
| 21 . | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2281 LF | RTP Company | PEEK | RTP |
| PROTEQ™ G30H283 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| UNITIKA Nylon 6 A1030TF | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| Durez® 33553 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| ALTECH® PA66 ECO 2020/116 GF20 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |