ALTECH® PP-H ECO 2030/552 GF30
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PP-H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bsb8O7_ALTECHPPHECO2030552GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH®PP-H ECO 2030/552 GF30 is a polypropylene homopolymer (PP Homopoly) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALTECH®PP-H ECO 2030/552 GF30 applications include the housing and automotive industries. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 42 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 126 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 80 - 120 | °C | |
| Hot air dryer | 80 - 120 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 200 - 270 | °C | |
| Mold Temperature | 20 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® A700 | Celanese Corporation | LCP | VECTRA® |
| DINALON® B1S25 C30-4152 | Grupo Repol | Nylon 6 | DINALON® |
| LNP™ LUBRICOMP™ KP004AXZ compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ LUBRICOMP™ |
| LONGLITE® PBT 5630F-104C | CCP Group | PBT | LONGLITE® PBT |
| Pinnacle PP 5135I3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |