INSTRUC PCABS
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bsMhVQ_INSTRUC-PCABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSTRUC PCABS is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 56.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 to 7.0 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 630 | J/m | ASTM D256 |
| Unnotched Izod Impact | > 2200 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 246 to 266 | °C | |
| Mold Temperature | 51.7 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.051 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 21Z | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Yuyao PA 03ML20 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| Geon™ Vinyl Flexible XV3860 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Lucon® CP6052 | LG Chem Ltd. | PC+ABS | Lucon® |
| POLLITE 1002G20 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |