Sunny® PBT EN200
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bqRWWR_Sunny-PBT-EN200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP reinforced polybutylene terephthalate |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.36 | g/cm³ | ASTM D792 |
| 23°C | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.3 to 1.8 | % | ASTM D955 |
| 23°C | 1.3 to 1.8 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 46.0 | MPa | ASTM D638 |
| -- | 46.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 19 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 1750 | MPa | ASTM D790 |
| -- 4 | 1800 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 58.0 | MPa | ASTM D790 |
| -- 5 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 6 | 6.0 | kJ/m² | ISO 180/1A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 115 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 235 | °C | |
| Front Temperature | 220 | °C | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 3.2mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hifax CA 1110 G4 LS | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Jam PE 60507 | Jam Petrochemical Company | HDPE | Jam PE |
| Karina BLUE PVC COMPOUND 800-06/230-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ RV008S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| POCAN® ECO T 3215 000000 | LANXESS GmbH | PBT+PET | POCAN® |